INSIZE 9646-301 Ultrasonic hardness testers (With bluetooth printer)

Specification

Data printout:with bluetooth printer

Main test parameter:HV

Convertible parameters:HRA, HRB, HRC, HBW, HS, MPa

Measurement range:50~1599HV, 20~68HRC, 85~650HB, 41~100HRB

61~85.6HRA, 34.2~97.3HS, 255~2180MPa

Resolution:1HV, 0.1HRA, 0.1HRB, 0.1HRC, 1HB, 0.1HS, 1MPa

Accuracy:±4%HV, ±4%HB, ±1.5HR

Calibration method:

Normal material: one-point calibration

Special materials: multi-point calibration

Operating temperature:-10°C ~ 40°C

Power supply:built-in rechargeable lithium battery (for 10 hours working)

Dimension of main unit:190×82×30mm

Dimension of probe:150xØ22mm

Weight:540g

Standard delivery

Main unit:1pc

19.6N manual probe:1pc

Bluetooth printer:1pc

charger:1pc

USB cable:1pc

Randomized standard hardness block:1pc

- Small size, light weight, portable, convenient for on-line measurement and can be used to measure large workpieces 

- Support 360°measurement, fast test speed, the fastest results in 1 second

- Standard Vickers indentation, small test indentation and low damage to the workpiece

- 100 measurement data sets and 10 calibration data sets can be stored

- Large display, directly shows the current measured value, maximum value, minimum value, average value and unit conversion value

- For unspecified conversion tables and unknown materials, multi-point calibration on any hardness scale you can choose to eliminate of systematic errors due to conversion tables 

- According to DIN 50159, ASTM A1038 standards

Applications:

1. Hardness measurement of flange edges and gearoot stampings, gears and gear grooves with hardened die sheet surfaces, taper sections

2. Hardness measurement of shafts and thin-walled pipes and vessels

3. Hardness measurement of thin plated layers, wheels, turbine rotors and welded parts

4. Measurement of the depth of a certain hole diameter deep holes, curvature of the larger dents and convex marks, irregular planes

5. Covering the majority of hardness measurement of industrial production of ferrous metals, non-ferrous metals and their alloys

Datasheet